The melting process of the material is optimized, so as to increase the extrusion yield and realize the extrusion of the material melt at a lower temperature.
Good homogenization of the material is achieved by the specific shear action in the isolation gap.
The melt plasticization process is controlled, meaning that only particles smaller than the isolation gap can enter the melt channel.
Material: 38 crmoala
Process: nitriding and bimetallic
Nitriding depth: 0.5mm-0.7mm
Bimetallic screw: alloy layer hardness HRC>60
Nitriding layer hardness: HV960-1100
Alloy layer depth: 2~2.5
Screw straightness: 0.015mm
Chrome plated screw: Chromium layer thickness: 0.03-0.06mm
Surface finish: 0.04Ra/um~0.08Ra/um
Nitride brittleness: less than grade 2
Aspect ratio: 1: (33~42)
Professional screw barrel manufacturers
Service Hotline：
+86-0580-8052262
Domestic mail：[email protected]
International mail：[email protected]
Address：C-No.7?XIHOU?INDUSTRIAL?AGGLOMERATION,JINTANG?TOWN,DINGHAI?DISTRICT, ZHOUSHAN?CITY,ZHEJIANG?PROVINCE,CHINA
0580-8052262
0580-8052262